Due to the intrinsic nature of a heterogeneous and anisotropic microstructure of cement based materials and the small indentation size, the measured microhardness values are subject to considerable variability. This work presents an in-depth assessment of microhardness of hardened cement pastes（HCPs） from a statistical perspective. Hundreds of microhardness measurements were conducted on an HCP sample using a Vickers Microhardness Tester. The results showed that the microhardness measured from the HCP sample significantly scattered with a large standard deviation, varying from tens to hundreds. The data-set of microhardness values was not normally distributed but fit best with a three-parameter lognormal model. By using a statistical software, the probability density function of the microhardness distribution can be readily obtained. The arithmetic mean and its 95% confidence intervals of the measured microhardness values can be used to best represent the microhardness characteristics of HCPs.
Due to the intrinsic nature of a heterogeneous and anisotropic microstructure of cement based materials and the small indentation size, the measured microhardness values are subject to considerable variability. This work presents an in-depth assessment of microhardness of hardened cement pastes（HCPs） from a statistical perspective. Hundreds of microhardness measurements were conducted on an HCP sample using a Vickers Microhardness Tester. The results showed that the microhardness measured from the HCP sample significantly scattered with a large standard deviation, varying from tens to hundreds. The data-set of microhardness values was not normally distributed but fit best with a three-parameter lognormal model. By using a statistical software, the probability density function of the microhardness distribution can be readily obtained. The arithmetic mean and its 95% confidence intervals of the measured microhardness values can be used to best represent the microhardness characteristics of HCPs.
基金
the National Natural Science Foundation of China(Nos.51302191 and 51132010)