研究间-甲-白-钴粘合体系对天然橡胶(NR)/氯丁橡胶(CR)并用胶与镀铜钢丝粘合性能的影响。结果表明,选择NR/CR并用比为80/20,采用间-甲-白-钴粘合体系,当SL-3020/RA-65/白炭黑/硼酰化钴用量比为1/3/15/2时,NR/CR并用胶与镀铜钢丝的物理性能和粘合性能较好。
The effects of resorcinol-formaldehyde resin-silica-cobalt boroylate system on the adhesion property between NR/CR blend and brass plated steel wire were investigated. The results showed that when the blend ratio of NR/CR was 80/20 and the dosage ratio of SL-3020/RA-65/silica/cobalt boroylate was 1/3/15/2 in resorcinol-formaldehyde resin-silica-cobalt boroylate adhesion system,the physical properties of NR/CR blend and its adhesion property to brass plated steel wire were better.