Susceptibility and morphological characteristics of crevice corrosion for SS316, SS904L, SS254sMo and SS2507 in thesimulated low-temperature multi-effect distillation environment were investigated by cyclic polarization test, scanningelectron microscope and laser microscope. The results show that the crevice corrosion resistance of four kinds of stainlesssteel is ranked as SS254sMo ≈ SS2507 〉 SS316 〉 SS904L. There are ＂cover＂ structures over the edge of active crevicecorrosion regions of SS904L, SS254sMo and SS2507, but SS316 is an exception. Galvanic corrosion characteristicsappeared in the crevice of duplex supper stainless steel SS2507.
Susceptibility and morphological characteristics of crevice corrosion for SS316, SS904L, SS254sMo and SS2507 in thesimulated low-temperature multi-effect distillation environment were investigated by cyclic polarization test, scanningelectron microscope and laser microscope. The results show that the crevice corrosion resistance of four kinds of stainlesssteel is ranked as SS254sMo ≈ SS2507 〉 SS316 〉 SS904L. There are ＂cover＂ structures over the edge of active crevicecorrosion regions of SS904L, SS254sMo and SS2507, but SS316 is an exception. Galvanic corrosion characteristicsappeared in the crevice of duplex supper stainless steel SS2507.
基金
supported by the National High Technology Research and Development Program(‘‘863’’ Program)of China(No.2015AA034301)
the National Natural Science Foundation of China(No.51501201)