摘要
In order to predict flow instability of wear-resistant steel BTW1, the hot compressions of wear-resistant steel BTW1 were firstly performed at the temperature of 900-1150 ℃ and at the strain rate of 0.05-15 s-1. Then, the constitutive relation was established based on Arrhenius-type hyperbolic sine equation. The results demonstrated that the flow stress depended on the deformation temperature and strain rate. When the deformation temperature kept constant, the flow stress increased as the strain rate increased. When the strain rate remained constant, the flow stress decreased as the temperature increased. The flow stresses calculated by constitutive equations were in a good agreement with experimental results. The apparent activation energy for deformation in the above processing region was estimated to be 369 kJ tool-1. A processing map could be obtained by the superimposition of an instability map on a power dissipation map. Based on the analysis of processing map and the microstructures, the theological instability regimes of strain rate and temperature for hot deformation of wear-resistant steel BTWl had been identified.
In order to predict flow instability of wear-resistant steel BTW1, the hot compressions of wear-resistant steel BTW1 were firstly performed at the temperature of 900-1150 ℃ and at the strain rate of 0.05-15 s-1. Then, the constitutive relation was established based on Arrhenius-type hyperbolic sine equation. The results demonstrated that the flow stress depended on the deformation temperature and strain rate. When the deformation temperature kept constant, the flow stress increased as the strain rate increased. When the strain rate remained constant, the flow stress decreased as the temperature increased. The flow stresses calculated by constitutive equations were in a good agreement with experimental results. The apparent activation energy for deformation in the above processing region was estimated to be 369 kJ tool-1. A processing map could be obtained by the superimposition of an instability map on a power dissipation map. Based on the analysis of processing map and the microstructures, the theological instability regimes of strain rate and temperature for hot deformation of wear-resistant steel BTWl had been identified.
基金
This work was supported by the National Natural Science Foundation of China （No. U1510131） and the Applied Basic Research Project of Shanxi Province （Nos. 201701D121078 and 201701D221143）.