Nanoscale zero-valent iron （nZVI） assembled on graphene oxide （GO） （rGO-nZVI） composites were synthesized by reduction of GO and ferrous ions with potassium borohydride, for use in Cr（VI） removal from aqueous solution. The results showed that the two-dimensional structure of GO could provide a skeleton support for Fe0, thus overcoming the bottleneck of aggregation for nZVI. Also, rGO-nZVI would form a ferric-carbon micro-electrolysis system in Cr（VI）-contaminated aquifers, enhancing and accelerating electron transfer, exhibiting high rate and capacity for Cr（VI） removal. The optimum dosage of the applied rGO-nZVI was linearly correlated with the initial Cr（VI） concentration. Characterization of rGO-nZVI before and after reaction with Cr（VI） revealed the process of Cr（VI） removal： rGO-nZVI firstly transferred electrons from Fe0 cores via their Fe（II）/Fe（III） shells to the GO sheet; there, negatively charged Cr（VI） received electrons and changed into positively charged Cr（III）, which was adsorbed by the negatively charged GO sheet, avoiding the capping and passivating of nZVI rGO-nZVI formed a good electrically conductive network, and thus had long-term electron releasing properties, which was important for groundwater remediation.
Nanoscale zero-valent iron （nZVI） assembled on graphene oxide （GO） （rGO-nZVI） composites were synthesized by reduction of GO and ferrous ions with potassium borohydride, for use in Cr（VI） removal from aqueous solution. The results showed that the two-dimensional structure of GO could provide a skeleton support for Fe0, thus overcoming the bottleneck of aggregation for nZVI. Also, rGO-nZVI would form a ferric-carbon micro-electrolysis system in Cr（VI）-contaminated aquifers, enhancing and accelerating electron transfer, exhibiting high rate and capacity for Cr（VI） removal. The optimum dosage of the applied rGO-nZVI was linearly correlated with the initial Cr（VI） concentration. Characterization of rGO-nZVI before and after reaction with Cr（VI） revealed the process of Cr（VI） removal： rGO-nZVI firstly transferred electrons from Fe0 cores via their Fe（II）/Fe（III） shells to the GO sheet; there, negatively charged Cr（VI） received electrons and changed into positively charged Cr（III）, which was adsorbed by the negatively charged GO sheet, avoiding the capping and passivating of nZVI rGO-nZVI formed a good electrically conductive network, and thus had long-term electron releasing properties, which was important for groundwater remediation.
基金
supported by the National Natural Science Foundation of China(Nos.41772244 and 41530636)