摘要
Industrial application of superhydrophobic surfaces is often hindered by complicated process and sophisticated machines. A facile wet etching method （sandblast, HCl and sandblast/HCl） with vapor deposition of PFDS （1H, 1H, 2H, 2H- perfluorodecyltriethoxysilane） was applied to fabricate superhydrophobic surface of heat-resistant steel used for vane. The coating component, surface morphology and surface roughness parameters of sample were observed by attenuated total reflectance Fourier transform infrared spectroscopy, scanning electron microscopy and atomic force microscopy. Static water contact angle （WCA） of samples with and without PFDS coating was measured by contact angle goniometer. The results showed that WCA values of polished, sandblast, HCl and sandblast/HCl-etched samples are 98°, 97°, 100° and 101°, respectively, and increase to 112°, 148°, 151 ° and 154v after vapor deposition of PFDS. The sandblast/HCl-etched sample with PFDS coating shows higher superhydrophobicity because of very large surface roughness and lotus protrusionlike structure. The superhydrophobicity of this fabricated surface has no obvious change after 38 cycles of the film adhesion test, indicating excellent durability.
Industrial application of superhydrophobic surfaces is often hindered by complicated process and sophisticated machines. A facile wet etching method （sandblast, HCl and sandblast/HCl） with vapor deposition of PFDS （1H, 1H, 2H, 2H- perfluorodecyltriethoxysilane） was applied to fabricate superhydrophobic surface of heat-resistant steel used for vane. The coating component, surface morphology and surface roughness parameters of sample were observed by attenuated total reflectance Fourier transform infrared spectroscopy, scanning electron microscopy and atomic force microscopy. Static water contact angle （WCA） of samples with and without PFDS coating was measured by contact angle goniometer. The results showed that WCA values of polished, sandblast, HCl and sandblast/HCl-etched samples are 98°, 97°, 100° and 101°, respectively, and increase to 112°, 148°, 151 ° and 154v after vapor deposition of PFDS. The sandblast/HCl-etched sample with PFDS coating shows higher superhydrophobicity because of very large surface roughness and lotus protrusionlike structure. The superhydrophobicity of this fabricated surface has no obvious change after 38 cycles of the film adhesion test, indicating excellent durability.