Based on the extended application of COMSOL multiphysics, a novel dual heat source model for pulsed laser-gas tungsten arc （GTA） hybrid welding was established. This model successfully solved the problem of simulation inaccuracy caused by energy superposition effect between laser and arc due to their different physical characteristics. Numerical simulation for pulsed laser-GTA hybrid welding of magnesium alloy process was conducted, and the simulation indicated good agree- ments with the measured thermal cycle curve and the shape of weld beads. Effects of pulse laser parameters （laser-excited current, pulse duration, and pulse frequency） on the temperature field and weld pool morphology were investigated. The experimental and simulation results suggest that when the laser pulse energy keeps constant, welding efficiency of the hybrid heat source is increased by increasing laser current or decreasing pulse duration due to the increased ratio of the weld bead depth to width. With large laser currents, severe spatters tend to occur. For optimized welding process, the laser current should be controlled in the range of 150-175 A, the pulse duration should be longer than 1 ms, and the pulse frequency should be equal to or slightly greater than 20 Hz.
Based on the extended application of COMSOL multiphysics, a novel dual heat source model for pulsed laser-gas tungsten arc （GTA） hybrid welding was established. This model successfully solved the problem of simulation inaccuracy caused by energy superposition effect between laser and arc due to their different physical characteristics. Numerical simulation for pulsed laser-GTA hybrid welding of magnesium alloy process was conducted, and the simulation indicated good agree- ments with the measured thermal cycle curve and the shape of weld beads. Effects of pulse laser parameters （laser-excited current, pulse duration, and pulse frequency） on the temperature field and weld pool morphology were investigated. The experimental and simulation results suggest that when the laser pulse energy keeps constant, welding efficiency of the hybrid heat source is increased by increasing laser current or decreasing pulse duration due to the increased ratio of the weld bead depth to width. With large laser currents, severe spatters tend to occur. For optimized welding process, the laser current should be controlled in the range of 150-175 A, the pulse duration should be longer than 1 ms, and the pulse frequency should be equal to or slightly greater than 20 Hz.
基金
This work was supported by the Natural Science Foundation of Liaoning Province of China （Grant Nos. 201602391 and 20170540460）.