以碳钢P265GH和不锈钢321为试验对象,结果表明,在相同焊接工艺参数下,涂刷配制出的活性剂,可大大增加焊接焊缝熔深,对于板件厚度在8 mm以下时,可无需开坡口、不用填丝,一次完成焊接过程,单面焊双面成形.并对焊缝接头进行相关的物理、化学分析,得到的焊缝宏观成形良好、熔深明显较常规TIG大,微观金相组织、力学性能均满足核电安装的焊接要求.
Taking carbon steel P265GH and stainless steel 321 as test objects,the results show that under the same welding process parameters, the flux prepared by brushing can greatly increase the weld penetration depth. When the thickness of plate is below 8 mm, there is no need for opening groove and no wire filling.The welding process is completed once ,one side welding and two sides forming.Through the physical and chemical analysis of the weld joint, the results show that the weld is formed well, the penetration is obviously larger than that of the conventional TIG, and the mierostrueture and mechanical properties of the weld meet the welding requirements of nuclear power installation.
作者
张攀
王湘江
ZHANG Pan;WANG Xiangjiang(School of Mechanical Engineering,University of South China,Hengyang,Hunan 421001,China;Hunan Provincial Key Laboratory of Emergency Sat~ty Technology and Equipment for Nuclear Facilities,University of South China,Hengyang,Hunan 421001,China)
出处
《南华大学学报(自然科学版)》
2018年第5期76-80,共5页
Journal of University of South China:Science and Technology
基金
南华大学研究生科学基金资助项目(2018kyz013)
关键词
活性剂配比
A—TIG
焊缝性能
碳钢和不锈钢
active agent ratio
A-TIG wehling
weht performance
earbon steel and stainless steel