摘要
研究不同牌号的炭黑对氯丁橡胶(CR)硫化胶物理性能以及CR与黄铜粘合力的影响。结果表明:采用炭黑N330或N234的CR硫化胶具有较好的物理性能;无论是物理粘合法还是化学粘合法,采用炭黑N550胶料的初始抽出力、热老化抽出力以及水浸泡后抽出力均最大。
The effects of different grades of carbon black on the physical properties of chloroprene rubber（CR）vulcanizate and the adhesion between CR and brass were investigated. The results showed that,the CR vulcanizate with good physical properties could be obtained when carbon black N330 or N234 was used. With carbon black N550 filled compound,the pull-out forces before and after thermal aging or water immersion were the largest with either physical or chemical treatment method.
作者
米广杰
于凯本
李天涯
林广义
MI Guangiie;YU Kaiben;LI Tianya;LIN Guangyi(Taishan Vocational and Technical College,Taian 271001,China;National Deep-sea Base Management Center,Qingdao 266237,China;Qingdao University of Science and Technology,Qingdao 266061,China)
出处
《橡胶工业》
CAS
2018年第11期1214-1217,共4页
China Rubber Industry
基金
山东省自然科学基金资助项目(ZR2013EMM002)
山东省轮胎与橡胶协同创新中心项目(2014G7R0015)
关键词
氯丁橡胶
炭黑
物理性能
粘合力
热老化
水浸泡
chloroprene rubber
carbon black
physical property
adhesive force
thermal aging
water immersion