摘要
以混合元素粉末为原料,采用激光立体成形(Laser solid forming, LSF)技术制备新型Ti-6Al-6Mo合金。研究了沉积态试样的显微组织以及固溶时效处理对合金显微组织形成及硬度的影响。结果表明,本研究所采用的热处理制度对原始β晶粒形貌没有显著的影响;固溶温度、固溶时间和固溶后的冷却方式对原始β晶粒中α相的形貌和尺寸以及LSFTi-6Al-6Mo合金的显微硬度均有显著影响。当时效时间超过4 h后,随着时效时间的延长,合金的显微组织和显微硬度均未产生明显变化。基于不同热处理条件下LSF Ti-6Al-6Mo合金中初生α板条和次生α板条的析出机制及其对β基体的强化作用分析,揭示了热处理对LSFTi-6Al-6Mo合金的显微组织和显微硬度的影响机理。
A novel Ti-6 Al-6 Mo alloy sample was fabricated by laser solid forming(LSF) using blended elemental powders as raw material. The microstructure of the as-deposited sample was investigated, and the effects of solution and aging treatment on the microstructure and microhardness of LSF Ti-6 Al-6 Mo alloy were discussed. The results show that the heat treatment conducted in this study has no obvious effect on the morphologies of prior ? grains of the alloy. The solution temperature, solution time, and cooling method after solution treatment have a significant effect on the morphology and size of α phase in the prior β grains and the microhardness of the LSF Ti-6 Al-6 Mo alloy. When the aging time exceeds 4 h, the microstructure and microhardness of the alloy change little with aging time. Based on the precipitation mechanism of the primary α laths and secondary α laths and their strengthening effect on the ? matrix in LSF Ti-6 Al-6 Mo alloy under different heat treatment conditions, the influence mechanism of heat treatment on the microstructure and microhardness of LSF Ti-6 Al-6 Mo was revealed.
作者
张凤英
胡腾腾
谭华
邱莹
梅敏
杨海欧
Zhang Fengying;Hu Tengteng;Tan Hua;Qiu Ying;Mei Min;Yang Haiou(Chang’an University,Xi’an 710064,China;State Key Laboratory of Solidification Processing,Northwestern Polytechnical University,Xi’an 710072,China)
出处
《稀有金属材料与工程》
SCIE
EI
CAS
CSCD
北大核心
2019年第2期357-365,共9页
Rare Metal Materials and Engineering
基金
National Key Basic Research Development Program of China(2016YFB1100103)
China Postdoctoral Science Foundation(2016M592731)
Fundamental Research Funds for the Central Universities(300102319208,300102318205)
National Training Program of Innovation and Entrepreneurship for Undergraduates(201810710119)