通过粉末冶金法制备了Ag-SnO_2 触头材料。选择Bi_2O_3、TiO 2和CeO 2为添加剂,每种添加剂选取4种粒度,添加剂的比例通过润湿性试验获得。对掺杂不同种类不同粒度的Ag-SnO_2 触头材料的物理和电接触性能进行了研究。结果表明,3种添加剂(Bi_2O_3、TiO 2和CeO_2 )的粒度对触头材料性能的影响趋势是一致的,随着添加剂粒度的减小,Ag-SnO_2 触头材料的物理和电接触性能都得到了提高,并且添加剂的最佳粒径为200 nm。
Ag-SnO2 contact materials were prepared by powder metallurgy technology. Bi2O3, TiO2 and CeO2 were chosen as additives, and four kinds of particle sizes were selected. Meanwhile, the proportion of additives was selected through wetting ability tests. The physical and electrical contact properties of Ag-SnO2 contact materials doped with additives of different kinds and particle sizes were studied. The results show that the influence of particle sizes of three additives(Bi2O3, TiO2 and CeO2 ) on the properties of Ag-SnO2 contact materials is consistent. With the decrease of additive particle size, the physical and electrical contact properties of Ag-SnO2 contact materials are improved, and the optimal particle size of additive is 200 nm.
作者
王海涛
王连峥
王子相
Wang Haitao;Wang Lianzheng;Wang Zixiang(State Key Laboratory of Reliability and Intelligence of Electrical Equipment,Key Laboratory of Electromagnetic Field and Electrical Apparatus Reliability of Hebei Province,Hebei University of Technology,Tianjin 300130,China)
出处
《稀有金属材料与工程》
SCIE
EI
CAS
CSCD
北大核心
2019年第2期458-462,共5页
Rare Metal Materials and Engineering
基金
Natural Science Foundation of Hebei(E2016202106)
Science and Technology Research Project of Hebei Higher Education(ZD2016078)
Tianjin Science and Technology Development Fund Project(20140419)
关键词
Ag-SnO2触头材料
润湿性
添加剂粒度
物理特性
接触电阻
Ag-SnO2 contact materials
wetting ability
additive particle size
physical properties
contact resistance