摘要
为了提高锰酸锂的比容量和循环性能,以四氧化三锰代替电解二氧化锰(EMD),同时进行元素掺杂,并利用正交实验法优化四氧化三锰和碳酸锂固相合成锰酸锂工艺。最终得到比容量110mA·h/g,常温25℃1C循环500次容量保持率为97.3%的锰酸锂产品。
In order to improve the specific capacity and cycle performance of LiMn2O4,Mn3O4 was used instead of EMD,and element doping was carried out at the same time.Orthogonal experiment was used to optimize the solid-state synthesis process of LiMn2O4 from Mn3O4 and lithium carbonate.Finally,LiMn2O4 with specific capacity of 110 mA·h/g and capacity retention rate of 97.3%for 500 cycles at 1 Crate at 25℃are obtained.
作者
王志鹏
杨洋
王以存
马金保
WANG Zhi-peng;YANG Yang;WANG Yi-cun;MA Jin-bao(Sinosteel Anhui Tianyuan Technology Co.,Ltd Magnetic Material Plant,Maanshan,Anhui 243000,China)
出处
《电池工业》
CAS
2018年第5期244-247,共4页
Chinese Battery Industry