Magnetic properties of nanostructural γ-Ni-28Fe alloy

Nanostructural γ-Ni-28Fe alloy(nano γ-Ni-28Fe)was successfully prepared by mechanochemical alloying(MCA).The relationship between the microstructure and the synthesis conditions was investigated by using XRD,TEM,SEM as well as BET analyzer.The results show that nano γ-Ni-28Fe alloy is composed of a gamma phase(FCC structure).Its grain size is about 20 nm at reduction temperature below 600 ℃.The magnetic measurements indicate that the saturation magnetization of nano γ-Ni-28Fe alloy is 102.4 A·m2/kg,and the coercivity is much higher than that of conventional coarse-grained counterpart.The result may be attributed to its decrease of the grain size and chemical composition in nano γ-Ni-28Fe alloy.

Nanostructural γ-Ni-28Fe alloy (nano γ-Ni-28Fe) was successfully prepared by mechanochemical alloying(MCA). The relationship between the microstructure and the synthesis conditions was investigated by using XRD, TEM, SEM as well as BET analyzer. The results show that nano γ-Ni-28Fe alloy is composed of a gamma phase (FCC structure). Its grain size is about 20 nm at reduction temperature below 600 °C. The magnetic measurements indicate that the saturation magnetization of nano γ-Ni-28Fe alloy is 102.4 A·m2/kg, and the coercivity is much higher than that of conventional coarse-grained counterpart. The result may be attributed to its decrease of the grain size and chemical composition in nano γ-Ni-28Fe alloy.