摘要
The corrosion mechanism of high ferric oxide slag to the magnesia-carbon brick for UHP furnace was analyzed,and the magnesia-carbon brick with high ferric oxide slag resistance was develped by selecting specially processed fused magnesite and changing size distrbution and the additives.The magnesia-carbon brick has good affinity to the slag and could adhere the slag efficiently in usage,It has better slag corrosion resistance and high temperature strength than the ordinary magnesia-carbon brick It showed better adaptable to the high ferric oxide slag when it was first used in 1999 in 150t UHP furnace of Tianjing Steel Pipe Company ,and achieved 400 heats service life.