摘要
This paper describes the resisting ability of gunning material for blast furnace to carbon monoxide corrosion under the mixed gas condition through inletting hydrogen into pure CO . A standard for testing ike resisting ability of refractory to CO corrosion with mixed gas instead of pure CO has also been discussed. The results show : the addition of hydrogen accelerates the CO corrosion on gunning material ; the same results has been reached with the CO , 200 hours and CO 95 % + H2 5 % , 24 hours. It is reasonable to use CO 95% + H25% , 24 hours instead of pure CO, 200 hours to lest the resisting ability of refractory to carbon monoxide corrosion.
This paper describes the resisting ability of gunning material for blast furnace to carbon monoxide corrosion under the mixed gas condition through inletting hydrogen into pure CO . A standard for testing ike resisting ability of refractory to CO corrosion with mixed gas instead of pure CO has also been discussed. The results show : the addition of hydrogen accelerates the CO corrosion on gunning material ; the same results has been reached with the CO , 200 hours and CO 95 % + H2 5 % , 24 hours. It is reasonable to use CO 95% + H25% , 24 hours instead of pure CO, 200 hours to lest the resisting ability of refractory to carbon monoxide corrosion.