Gold colloids were prepared by citrate-induced reduction of hydrogen tetrachloroaurale, and gold nanoparticles were electrostatically self-assembled with poly( diallyldimethylammonium chloride) into multi-layer thin films on si/icon and quartz substrates. The paniculate thin films were characterized by UV-vis spea-troscopy, surface, enhanced Raman scattering, atomic force microscopy and resistivity measurements. Due to the interparticle coupling between individual gold particles, an obvious collective particle plasmon resonance was ob-served on UV-vis spectra , and the particulate thin films exhibited a strong SERS effect. For multilayer thin films with a high particle coverage on substrates , resistivity of the order of 10-4 Ω·cm was yielded.
Gold colloids were prepared by citrate-induced reduction of hydrogen tetrachloroaurale, and gold nanoparticles were electrostatically self-assembled with poly( diallyldimethylammonium chloride) into multi-layer thin films on si/icon and quartz substrates. The paniculate thin films were characterized by UV-vis spea-troscopy, surface, enhanced Raman scattering, atomic force microscopy and resistivity measurements. Due to the interparticle coupling between individual gold particles, an obvious collective particle plasmon resonance was ob-served on UV-vis spectra , and the particulate thin films exhibited a strong SERS effect. For multilayer thin films with a high particle coverage on substrates , resistivity of the order of 10-4 Ω·cm was yielded.
基金
This research was financially supported by China Scholar-ship Council and the Natural Science Foundation of Hubei Province (Project 2000J002)