摘要
Al62.5Cu25Fe12.5 alloy was prepared by arc melting. It was found that the formation of quasicrystalline phase is related to the condition of annealing, such as temperature and duration. Weight gain of AI-Cu-Fe quasicrystal during the oxidation at 700 and 800℃ in dry air was measured by means of thermal balance. The oxidation kinetics showed that the quasicrystal has good oxidation resistance. Only α-Al2O3 was formed on Al62.5Cu25Fe12.5 quasicrystal. The surface morphologies of AI-Cu-Fe quasicrystal after isothermal oxidation for different times were observed.
基金
The Aviation Science Foundation of China is acknowledged forfinaricial aupport urder Grant No.0OH51006.