摘要
以Ti6Al4V钛合金粉末为研究对象,在单层扫描和单道扫描实验的基础上,研究SLM工艺参数对Ti6Al4V合金材料成型性的影响,并进行了块体成型实验,通过设计正交试验及观察试样的形貌和致密度分析,最终得到Ti6Al4V合金粉末SLM块体成型的最佳工艺参数为:激光功率400W、搭接率1、扫描速度750mm/min,其致密度可以达到96.17%。
Taking Ti6Al4V titanium alloy powder as the research object,on the basis of single layer scanning and single channel scanning experiment,this paper studies the influence of selective laser melting(SLM)process parameters on Ti6Al4V alloy material formability,and block forming experiment is carried out.Through the design of orthogonal experiment,morphology observation of sample and density analysis,results show that the best block molding parameters of SLM technology in Ti6Al4V alloy powder are laser power of 400 W,lap rate of 1 and the scanning speed of 750 mm/min,density can up to 96.17%.