摘要
In this report,the microstructure,mechanical properties,and textures of warm rolled interstitial-free steel annealed at four different temperatures(730,760,790,and 820°C)were studied.The overall structural features of specimens were investigated by optical microscopy,and the textures were measured by X-ray diffraction(XRD).Nano-sized precipitates were then observed by a transmission electron microscope(TEM)on carbon extraction replicas.According to the results,with increased annealing temperatures,the ferrite grains grew;in addition,the sizes of Ti_4C_2S_2 and Ti C precipitates also increased.Additionally,the sizes of Ti N and Ti S precipitates slightly changed.When the annealing temperature increased from 730 to 820°C,the yield strength(YS)and the ultimate tensile strength(UTS)showed a decreasing trend.Meanwhile,elongation and the strain harden exponent(n value)increased to 49.6%and 0.34,respectively.By comparing textures annealed at different temperatures,the intensity of{111}texture annealed at 820°C was the largest,while the difference between the intensity of{111}<110>and{111}<112>was the smallest when the annealing temperature was 820°C.Therefore,the plastic strain ratio(r value)annealed at 820°C was the highest.
In this report,the microstructure,mechanical properties,and textures of warm rolled interstitial-free steel annealed at four different temperatures(730,760,790,and 820°C)were studied.The overall structural features of specimens were investigated by optical microscopy,and the textures were measured by X-ray diffraction(XRD).Nano-sized precipitates were then observed by a transmission electron microscope(TEM)on carbon extraction replicas.According to the results,with increased annealing temperatures,the ferrite grains grew;in addition,the sizes of Ti_4C_2S_2 and Ti C precipitates also increased.Additionally,the sizes of Ti N and Ti S precipitates slightly changed.When the annealing temperature increased from 730 to 820°C,the yield strength(YS)and the ultimate tensile strength(UTS)showed a decreasing trend.Meanwhile,elongation and the strain harden exponent(n value)increased to 49.6%and 0.34,respectively.By comparing textures annealed at different temperatures,the intensity of{111}texture annealed at 820°C was the largest,while the difference between the intensity of{111}<110>and{111}<112>was the smallest when the annealing temperature was 820°C.Therefore,the plastic strain ratio(r value)annealed at 820°C was the highest.