氧化石墨烯整理对粘胶织物性能的影响

Properties influences of viscose fabric finished by oxidized graphene

探讨了氧化石墨烯对粘胶织物整理前后织物性能的变化。研究表明:粘胶织物经氧化石墨烯整理后,织物表面比电阻值降低了8个数量级,极大地改善了粘胶织物的抗静电性能;导热性能与抗紫外线性能分别提高了38.9%与61倍多,同时整理后粘胶织物的断裂强力变化幅度仅为4.4%,因此氧化石墨烯整理很好的改善了粘胶织物的功能性,是一种较为理想的功能性整理工艺。综合考虑整理后粘胶织物的性能与整理工艺成本,认为当粘胶织物表面氧化石墨烯覆盖量达到250 mg/m^2为最佳覆盖量。

Properties influences of viscose fabric finished by oxidized graphene were studied by testing viscose fabrics properties of electric conduction,heat conduction,uvioresistant and mechanics before and after oxidized graphene finish.Research showed that properties of fabric superficies was decreased 8 order of magnitudes which properties of electric conduction was improved greatly;properties of fabric heat conduction and uvioresistant was increased 38.9%and 61 times and breaking strength was decreased 4.4%.All these modification data of properties of viscose fabric finished by oxidized graphene were demonstrated that viscose fabric finished by oxidized graphene was a perfect way of functional modification finish.Considering the properties of the viscose fabric after finishing and processing cost,it was believed that the best oxidized graphene overlay quantity was 250 mg/m2.