摘要
Ti-6 Al-4 V-Si3 N4 composites were effectively fabricated by spark plasma sintering(SPS) technique. The addition of Si_3 N_4 on Ti-6 AI-4 V was varied from 5% to 15%(wt fraction). The effect of Si_3 N_4 addition on the densification, microstructure, and microhardness and corrosion behaviour of Ti-6 Al-4 V was investigated.An increase in microhardness value was recorded from 325.46 HV_(0.1) to 585.73 HV_(0.1). X-ray diffraction(XRD) analysis showed that the intensity of diffraction peaks of Si3 N4 phase in the composites increased.The sintered Ti-6 Al-4 V reinforced with Si_3 N_4 compacts revealed the non-existence of intermediate phases, such as TiSi_2(titanium silicide) which was expected. SEM analysis of the spark plasma sintered composites revealed a and β phase microstructures in Ti-6 Al-4 V with uniform distribution of Si3 N4 particulates in the matrix. The corrosion resistance property of the material was improved by the addition of Si_3 N_4 from 0.986629 mm/year to 0.030547 mm/year.
Ti-6 Al-4 V-Si3 N4 composites were effectively fabricated by spark plasma sintering(SPS) technique. The addition of Si_3 N_4 on Ti-6 AI-4 V was varied from 5% to 15%(wt fraction). The effect of Si_3 N_4 addition on the densification, microstructure, and microhardness and corrosion behaviour of Ti-6 Al-4 V was investigated.An increase in microhardness value was recorded from 325.46 HV_(0.1) to 585.73 HV_(0.1). X-ray diffraction(XRD) analysis showed that the intensity of diffraction peaks of Si3 N4 phase in the composites increased.The sintered Ti-6 Al-4 V reinforced with Si_3 N_4 compacts revealed the non-existence of intermediate phases, such as TiSi_2(titanium silicide) which was expected. SEM analysis of the spark plasma sintered composites revealed a and β phase microstructures in Ti-6 Al-4 V with uniform distribution of Si3 N4 particulates in the matrix. The corrosion resistance property of the material was improved by the addition of Si_3 N_4 from 0.986629 mm/year to 0.030547 mm/year.
基金
financial support from National Research Foundation(NRF), Pretoria, South Africa