紫外辐照聚酯纤维的概述 被引量:1

Overview of Ultraviolet Irradiation Polyester Fiber
下载PDF
导出
摘要 聚酯纤维在工业等各大领域应用更加广泛,但服役环境中存在紫外线的,会对聚酯纤维产生老化和破坏作用。本文主要概述了紫外辐照后,聚酯纤维的表观形貌的变化,力学性能降低,使用寿命降低。最后对提高聚酯纤维的抗紫外线辐照的前景和未来进行了展望。 Polyester fiber is widely used in various fields such as industry,but the presence of ultraviolet rays in the service environment will cause aging and damage to polyester fiber.This paper mainly summarizes the changes in apparent morphology and mechanical properties of polyester fibers after ultraviolet irradiation.Finally,the prospects and future of improving the anti-ultraviolet radiation of polyester fiber are prospected.
作者 闫民杰 许瑞 陈莉 梁振江 Minjie Yan;Rui Xu;Li Chen;Zhenjiang Liang(School of Textiles,Tianjin Polytechnic University,Tianjin,300387;Material Science and Engineering School,Tianjin Polytechnic University,Tianjin 300387)
出处 《西部皮革》 2018年第24期4-4,共1页 West Leather
关键词 聚酯纤维 紫外 辐照 polyester fiber ultraviolet irradiation
  • 相关文献

参考文献2

二级参考文献16

  • 1F.Segovia,C.Ferrer,M.D.Salvador,V.Amigo.Influence of processing variables on mechanical characteristics of Sunlight aged polyester-glass fibre composites[J].Polym.Degrad.Stab,2001 (71):179-184.
  • 2M.Edge,N.S.Allen and R.Wiles.lndetification of luminescent species contributing to the yellowing of poly(ethylene terephthalate) on degradation[J].Polymer,199506):227-234.
  • 3S.J.Chiu,W.H.Cheng.Thermal degradation and catalytic cracking ofpoly(ethylene terephthalate)[J].Polymer Degradation and Stability,1999(63):407-412.
  • 4T.Grossetete,A.Pdvaton.J.L.Gardet te,C.E.Hoyle,M.Ziemer,D.R.Fagerburg,H.Clauberg.Photochemical degradation of poly(ethylene terephthalate)-modified copolymer[J].Polymer,2000 (41):3541-3554.
  • 5G.J.M Fechine,M.S.Rabello,R.M.Souto-Maior.The effect ofultraviolet stabilizers on the photodegradation of poly (ethylene terephthalate)[J].Polym.Degrad.Stab.,2002(75):153-159.
  • 6Catherine Wilhelm,Jean-Luc Gardette.Infrared analysis of the photochemical behaviour of segmented polyurethanes:l.Aliphatic poly(ester-urethane)[J].Polymer,1997(38):4019-4031.
  • 7L.Costa,M.P.Luda,L.TrossareUi.Ultra high molecular weight polyethylene-II.thermal-and photo-oxidation[J].Polymer Degradation and Stability,1997(58):41-54.
  • 8Day M,Wiles DM.Photochemical degradation of poly(ethylene terephthalate)Ⅱ.Effect of wavelength and environment on the decomposition process[J].J.Appl Polym Sci,1972,(16):191-202.
  • 9Yashutaka Nagai,Takahiro Ogawa,Liu Yu Zhen,et al.Analysis of weathering of thermoplastic polyester elastomers Ⅰ.Polyetherpolyester elastomers [J].Polym Degrad Stab,1997,56:115-121.
  • 10Nagai Y,Ogawa T,NishimotoY,et al.Analysis of weathering of a thermoplastic polyester elastomer Ⅱ.Factors affecting weathering of a polyether-polyester elastomer[J].Polym Degrad Stab,1999,65:217-224.

共引文献4

同被引文献36

引证文献1

二级引证文献7

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部