摘要
Two aromatic co-polyamides were synthesized combining two diacid monomers containing bulky pendant groups, 5-(9,10-dihydro-9,10-ethanoanthracene-11,12-dicarboximido)isophthalic acid(DEAIA) and 5-tert-butylisophthalic acid(TERT), with 4,4′-(hexafluoroisopropylidene)dianiline(HFA) or 2,3,5,6-tetramethyl-1,4-phenylenediamine(Durene) by direct polycondensation. The structures of the obtained aromatic co-polyamides were confirmed by FTIR, Raman and 1 H-NMR. The co-copolyamide films, DHTH and DDTD, exhibited rms-roughness values between 0.94 and 1.60 nm, respectively. Moreover, they presented good thermal stability up to300 °C. Young's moduli of the co-polyamide films were between 4.1 and 4.3 GPa. X-ray diffraction results showed that the co-polyamide films were amorphous due to the incorporation of both bulky pendant groups, tert-butyl and dibenzobarrelene. The combination of bulky pendant groups provided intrinsically transparent co-polyamide films with a transmittance higher than 88% in the range of 400-780 nm.Due to these outstanding film and optical properties, they are suggested to be flexible substrates in applications for solar cell and other portable electronic devices.
Two aromatic co-polyamides were synthesized combining two diacid monomers containing bulky pendant groups, 5-(9,10-dihydro-9,10-ethanoanthracene-11,12-dicarboximido)isophthalic acid(DEAIA) and 5-tert-butylisophthalic acid(TERT), with 4,4′-(hexafluoroisopropylidene)dianiline(HFA) or 2,3,5,6-tetramethyl-1,4-phenylenediamine(Durene) by direct polycondensation. The structures of the obtained aromatic co-polyamides were confirmed by FTIR, Raman and 1 H-NMR. The co-copolyamide films, DHTH and DDTD, exhibited rms-roughness values between 0.94 and 1.60 nm, respectively. Moreover, they presented good thermal stability up to300 °C. Young's moduli of the co-polyamide films were between 4.1 and 4.3 GPa. X-ray diffraction results showed that the co-polyamide films were amorphous due to the incorporation of both bulky pendant groups, tert-butyl and dibenzobarrelene. The combination of bulky pendant groups provided intrinsically transparent co-polyamide films with a transmittance higher than 88% in the range of 400-780 nm.Due to these outstanding film and optical properties, they are suggested to be flexible substrates in applications for solar cell and other portable electronic devices.
基金
the financial support from CONACYT-México(No.248378)
CONACYT-México for the fellowship 427467
partially supported by the project "Fortalecimiento e internacionalización del doctorado en ciencias(Materiales Poliméricos)del CICY" FOMIX YUC 2014-C17-247046