摘要
High quality perovskite films with large columnar grains are greatly desired for efficient perovskite solar cells. Here, low volatility N-methyl-2-pyrrolidone(NMP) was added in MAI/IPA solution in a two-step spin-coating method, which promoted the conversion of lead iodide to perovskite. The perovskite films were annealed by a closed-steam annealing method to prolong the recrystallization process of perovskite films assisted by the residual NMP. It leaded to high quality CH_3NH_3PbI_3 perovskite films with large columnar grains due to its enhancement of the Oswald ripening. The large grain perovskite film leaded to efficient carrier transformation and injection, and low recombination. The photovoltaic performance of the perovskite solar cells was improved significantly.
High quality perovskite films with large columnar grains are greatly desired for efficient perovskite solar cells. Here, low volatility N-methyl-2-pyrrolidone(NMP) was added in MAI/IPA solution in a two-step spin-coating method, which promoted the conversion of lead iodide to perovskite. The perovskite films were annealed by a closed-steam annealing method to prolong the recrystallization process of perovskite films assisted by the residual NMP. It leaded to high quality CH_3NH_3PbI_3 perovskite films with large columnar grains due to its enhancement of the Oswald ripening. The large grain perovskite film leaded to efficient carrier transformation and injection, and low recombination. The photovoltaic performance of the perovskite solar cells was improved significantly.
基金
financially supported by the National Natural Science Foundation of China(Grant No.21463002)
Startup Funding of Distinguished Professorship of "1000 Talents Program"(31370086963030)
Shenzhen Jiawei Photovoltaic Lighting Co.,Ltd.
Tsinghua University Initiative Scientific Research Program(20161080165)
Natural Science Foundation of Xinjiang Uygur Autonomous Region(No.2016D01C008)
Opening Project of State Key laboratory of Crystal Material(No.KF1610)
Scientific Research Program of the Higher Education Institution of Xinjiang(XJEDU2017M038)