The relationship between the tensile properties and S(delta) phase precipitation in cast alloy IN625 was investigated in this paper. Although the influences of δ phase on the mechanical properties have been pointed out in our previous work, the relationship is still not directly determined due to the coexistence of γ"(gamma double prime) and δ precipitates. In order to exclude the effect from γ" phase, various fractions of δ precipitates with few γ" precipitates were obtained by a set of experimental alloys aging at 750 ℃, and tensile tests were conducted in parallel. The results showed that both yield strength and ultimate tensile strength increased nearly in linear with increasing δ phase fraction, while the elongation was relatively and limitedly affected by δ precipitation when the area fraction of δ phase was above 10%.
The relationship between the tensile properties and S(delta) phase precipitation in cast alloy IN625 was investigated in this paper. Although the influences of δ phase on the mechanical properties have been pointed out in our previous work, the relationship is still not directly determined due to the coexistence of γ"(gamma double prime) and δ precipitates. In order to exclude the effect from γ" phase, various fractions of δ precipitates with few γ" precipitates were obtained by a set of experimental alloys aging at 750 ℃, and tensile tests were conducted in parallel. The results showed that both yield strength and ultimate tensile strength increased nearly in linear with increasing δ phase fraction, while the elongation was relatively and limitedly affected by δ precipitation when the area fraction of δ phase was above 10%.
基金
financially supported by the National Key Research and Development Program of China (No. 2017YFB0305204)
the National Natural Science Foundation of China (No. 51571191)