Two double cold reduction-drawn and redrawn(DRD) tinplate steels of the same chemistries that have been processed by continuous and batch annealing line have been researched. The composition of fibers were studied through X-ray diffraction. The results indicate that a strong intensity of {114}<110> was formed in the continuous annealing steel and a strong intensity of {111}<112> was formed in the batch annealing steel; not only that but the γ fiber slowly rotated to the low angel α fiber with the angel being about 30° nearly {112}<110>texture owing to the higher second reduction.
Two double cold reduction-drawn and redrawn(DRD) tinplate steels of the same chemistries that have been processed by continuous and batch annealing line have been researched. The composition of fibers were studied through X-ray diffraction. The results indicate that a strong intensity of {114}<110> was formed in the continuous annealing steel and a strong intensity of {111}<112> was formed in the batch annealing steel; not only that but the γ fiber slowly rotated to the low angel α fiber with the angel being about 30° nearly {112}<110>texture owing to the higher second reduction.
基金
Sponsored by the National Natural Science Foundation of China(Grant No.U1460101)