对实体工程中混凝土胀裂及钢筋锈蚀的分析与处理

Analysis and Treatment of Concrete Cracking and Steel Corrosion in Physical Engineering

某工程局部出现混凝土胀裂及钢筋锈蚀,通过对实体工程的现场调查与检测,混凝土开裂部位氯离子含量为0.63%~1.17%,且含量越高混凝土开裂现象越严重。论述该工程混凝土胀裂及钢筋锈蚀产生的原因,并提出具体的加固处理办法。

The concrete cracking and steel corrosion occurred in a project. Through the on-site investigation and inspection of the physical engineering, the chloride ion content of the concrete cracking part is 0.63%~1.17%, and the higher the content, the more serious the concrete cracking phenomenon. This paper discusses the causes of concrete cracking and steel corrosion in the project, and proposes specific reinforcement treatment methods.