摘要
Nanoscale zero-valent iron(n ZVI) particles supported on a porous, semi-interpenetrating(semi-IPN), temperature-sensitive composite hydrogel(PNIPAm-PHEMA). n ZVI@PNIPAmPHEMA, was successfully synthesized and characterized by FT-IR, SEM, EDS, XRD and the weighing method. The loading of nZVI was 0.1548 ± 0.0015 g/g and the particle size was30–100 nm. NZVI was uniformly dispersed on the pore walls inside the PNIPAm-PHEMA.Because of the well-dispersed n ZVI, the highly porous structure, and the synergistic effect of PNIPAm-PHEMA, nZVI@PNIPAm-PHEMA showed excellent reductive activity and wide p H applicability. 95% of 4-NP in 100 m L of 400 mg/L 4-NP solution with initial p H 3.0–9.0 could be completely reduced into 4-AP by about 0.0548 g of fresh supported n ZVI at 18–25 °C under stirring(110 r/min) within 45 min reaction time. A greater than 99% 4-NP degradation ratio was obtained when the initial p H was 5.0–9.0. The reduction of 4-NP by nZVI@PNIPAm-PHEMA was in agreement with the pseudo-first-order kinetics model with Kobsvalues of 0.0885–0.101 min-1.NZVI@PNIPAm-PHEMA was able to be recycled, and about 85% degradation ratio of 4-NP was obtained after its sixth reuse cycle. According to the temperature sensitivity of PNIPAmPHEMA, n ZVI@PNIPAm-PHEMA exhibited very good storage stability, and about 88.9%degradation ratio of 4-NP was obtained after its storage for 30 days. The hybrid reducer was highly efficient for the reduction of 2-NP, 3-NP, 2-chloro-4-nitrophenol and 2-chloro-4-nitrophenol. Our results suggest that PNIPAm-PHEMA could be a good potential carrier, with n ZVI@PNIPAm-PHEMA having potential value in the application of reductive degradation of nitrophenol pollutants.
Nanoscale zero-valent iron(n ZVI) particles supported on a porous, semi-interpenetrating(semi-IPN), temperature-sensitive composite hydrogel(PNIPAm-PHEMA). n ZVI@PNIPAmPHEMA, was successfully synthesized and characterized by FT-IR, SEM, EDS, XRD and the weighing method. The loading of nZVI was 0.1548 ± 0.0015 g/g and the particle size was30–100 nm. NZVI was uniformly dispersed on the pore walls inside the PNIPAm-PHEMA.Because of the well-dispersed n ZVI, the highly porous structure, and the synergistic effect of PNIPAm-PHEMA, nZVI@PNIPAm-PHEMA showed excellent reductive activity and wide p H applicability. 95% of 4-NP in 100 m L of 400 mg/L 4-NP solution with initial p H 3.0–9.0 could be completely reduced into 4-AP by about 0.0548 g of fresh supported n ZVI at 18–25 °C under stirring(110 r/min) within 45 min reaction time. A greater than 99% 4-NP degradation ratio was obtained when the initial p H was 5.0–9.0. The reduction of 4-NP by nZVI@PNIPAm-PHEMA was in agreement with the pseudo-first-order kinetics model with Kobsvalues of 0.0885–0.101 min-1.NZVI@PNIPAm-PHEMA was able to be recycled, and about 85% degradation ratio of 4-NP was obtained after its sixth reuse cycle. According to the temperature sensitivity of PNIPAmPHEMA, n ZVI@PNIPAm-PHEMA exhibited very good storage stability, and about 88.9%degradation ratio of 4-NP was obtained after its storage for 30 days. The hybrid reducer was highly efficient for the reduction of 2-NP, 3-NP, 2-chloro-4-nitrophenol and 2-chloro-4-nitrophenol. Our results suggest that PNIPAm-PHEMA could be a good potential carrier, with n ZVI@PNIPAm-PHEMA having potential value in the application of reductive degradation of nitrophenol pollutants.
基金
supported by the National Natural Science Foundation of China(No.51508233)
the Jiangsu Collaborative Innovation Center of Technology and Material of Water Treatment