Using cesium lead halide perovskite nanocrystals, CsPb(Cl/Br)3, as a light absorber, we report a highly effective UV and blue light blocking film. The CsPb(Cl/Br)3 nanocrystals are well dispersed in the ethyl cellulose(EC) matrix to compose a UV and blue light shielding film, and the absorption edge of the film is tunable by adjusting Cl to Br ratio using anion exchange. The CsPbCl2 Br-EC film exhibits a transmittance of 5% at 459 nm, 90% at 478 nm and 95% in the range of 500–800 nm, which makes it excellent for UV and blue light shielding. In addition, the as-prepared EC-CsPb(Cl/Br)3 film shows excellent photostability under UV irradiation. Results demonstrate that this EC-CsPb(Cl/Br)3 based materials with sharp absorbance edges, tunable blocking wavelength, and high photostability can be useful for the applications in UV and blue light blocking and optical filters.
Using cesium lead halide perovskite nanocrystals, CsPb(Cl/Br)3, as a light absorber, we report a highly effective UV and blue light blocking film. The CsPb(Cl/Br)3 nanocrystals are well dispersed in the ethyl cellulose(EC) matrix to compose a UV and blue light shielding film, and the absorption edge of the film is tunable by adjusting Cl to Br ratio using anion exchange. The CsPbCl2 Br-EC film exhibits a transmittance of 5% at 459 nm, 90% at 478 nm and 95% in the range of 500–800 nm, which makes it excellent for UV and blue light shielding. In addition, the as-prepared EC-CsPb(Cl/Br)3 film shows excellent photostability under UV irradiation. Results demonstrate that this EC-CsPb(Cl/Br)3 based materials with sharp absorbance edges, tunable blocking wavelength, and high photostability can be useful for the applications in UV and blue light blocking and optical filters
基金
financially supported by the National Nature Scientific Foundation of China(No.21675133)and OESACLS201902