Herein, we demonstrate that silica films with perpendicular macroporous channels and accessible ordered mesopores can be conveniently prepared. The hierarchical macroporous–mesoporous silica films are synthesized by using zinc oxide nanorod array as macroporous template and CTAB surfactant as mesoporous template. In basic surfactant-containing solution, ordered mesoporous silica shells homogeneously grow on the zinc oxide nanorod array. The growth of the mesostructures do not require any chemical modification for the zinc oxide nanorod, which opens a new way for preparing hierarchical silica films with perpendicular mesochannels. The prepared hierarchical macroporous–mesoporous silica films possess a uniform thickness of 2μm, large perpendicular macropores with a length of 1.8μm and a width of 80 nm, and accessible ordered mesopores. Separation experiment demonstrates that this macroporous–mesoporous film can effectively separate biomolecules with different sizes.
Herein, we demonstrate that silica films with perpendicular macroporous channels and accessible ordered mesopores can be conveniently prepared. The hierarchical macroporous–mesoporous silica films are synthesized by using zinc oxide nanorod array as macroporous template and CTAB surfactant as mesoporous template. In basic surfactant-containing solution, ordered mesoporous silica shells homogeneously grow on the zinc oxide nanorod array. The growth of the mesostructures do not require any chemical modification for the zinc oxide nanorod, which opens a new way for preparing hierarchical silica films with perpendicular mesochannels. The prepared hierarchical macroporous–mesoporous silica films possess a uniform thickness of 2 mm, large perpendicular macropores with a length of 1.8 mm and a width of 80 nm, and accessible ordered mesopores. Separation experiment demonstrates that this macroporous–mesoporous film can effectively separate biomolecules with different sizes.
基金
the financial support from the Natural Science Foundation of Jiangsu Province(No.BK20160017)
the National Natural Science Foundation of China(No.21603106)