摘要
通过L9(3^4)正交设计试验表进行正交试验,研究LN17模具钢预硬化热处理最优工艺参数。结果表明,采用1,020℃淬火、630℃回火4h预硬化处理,硬度值为30.2~30.7HRC,达到技术标准硬度28-32HRC的中值。
A study of Pre-hardening heat treatment parameter for LN 17 was conducted by orthogonal test of L9(3^4). Results showed that hardness of 30.2~30.7HRC were made by a optimum process of quenching at 1,020℃, tempering at 630℃for 4h.
作者
汝亚彬
胡永才
康爱军
刘宝石
秋立鹏
王琳
谭凯
郑继辉
于海鹏
赵越
Ru Yabin;Hu Yongcai;Kang Aijun;Liu Baoshi;Qiu Lipeng;Wang Lin;Tan Kai;Zheng Jihui;Yu Haipeng;Zhao Yue
出处
《模具制造》
2019年第7期84-86,共3页
Die & Mould Manufacture
关键词
模具钢
正交试验
预硬化处理
硬度
mold steel
orthogonal
test pre-hardening
hardness