摘要
BACKGROUND Stent insertion can effective alleviate the symptoms of benign esophageal strictures(BES).Magnesium alloy stents are a good candidate because of biological safety,but show a poor corrosion resistance and a quick loss of mechanical support in vivo.AIM To test the therapeutic and adverse effects of a silicone-covered magnesium alloy biodegradable esophageal stent.METHODS Fifteen rabbits underwent silicone-covered biodegradable magnesium stent insertion into the benign esophageal stricture under fluoroscopic guidance(stent group).The wall reconstruction and tissue reaction of stenotic esophagus in the stent group were compared with those of six esophageal stricture models(control group).Esophagography was performed at 1,2,and 3 weeks.Four,six,and five rabbits in the stent group and two rabbits in the control groups were euthanized,respectively,at each time point for histological examination.RESULTS All stent insertions were well tolerated.The esophageal diameters at immediately,1,2 and 3 wk were 9.8±0.3 mm,9.7±0.7 mm,9.4±0.8 mm,and 9.2±0.5 mm,respectively(vs 4.9±0.3 mm before stent insertion;P<0.05).Magnesium stents migrated in eight rabbits[one at 1 wk(1/15),three at 2 wk(3/11),and four at 3 wk(4/5)].Esophageal wall remodeling(thinner epithelial and smooth muscle layers)was found significantly thinner in the stent group than in the control group(P<0.05).Esophageal injury and collagen deposition following stent insertion were similar and did not differ compared to rabbits with esophageal stricture and normal rabbits(P>0.05).CONCLUSION Esophageal silicone-covered biodegradable magnesium stent insertion is feasible for BES without causing severe injury or tissue reaction.Our study suggests that insertion of silicone-covered magnesium esophageal stent is a promising approach for treating BES.
BACKGROUND Stent insertion can effective alleviate the symptoms of benign esophageal strictures(BES). Magnesium alloy stents are a good candidate because of biological safety, but show a poor corrosion resistance and a quick loss of mechanical support in vivo.AIM To test the therapeutic and adverse effects of a silicone-covered magnesium alloy biodegradable esophageal stent.METHODS Fifteen rabbits underwent silicone-covered biodegradable magnesium stent insertion into the benign esophageal stricture under fluoroscopic guidance(stent group). The wall reconstruction and tissue reaction of stenotic esophagus in the stent group were compared with those of six esophageal stricture models(control group). Esophagography was performed at 1, 2, and 3 weeks. Four, six, and five rabbits in the stent group and two rabbits in the control groups were euthanized,respectively, at each time point for histological examination.RESULTS All stent insertions were well tolerated. The esophageal diameters at immediately, 1, 2 and 3 wk were 9.8 ± 0.3 mm, 9.7 ± 0.7 mm, 9.4 ± 0.8 mm, and 9.2± 0.5 mm, respectively(vs 4.9 ± 0.3 mm before stent insertion; P < 0.05).Magnesium stents migrated in eight rabbits [one at 1 wk(1/15), three at 2 wk(3/11), and four at 3 wk(4/5)]. Esophageal wall remodeling(thinner epithelial and smooth muscle layers) was found significantly thinner in the stent group than in the control group(P < 0.05). Esophageal injury and collagen deposition following stent insertion were similar and did not differ compared to rabbits with esophageal stricture and normal rabbits(P > 0.05).CONCLUSION Esophageal silicone-covered biodegradable magnesium stent insertion is feasible for BES without causing severe injury or tissue reaction. Our study suggests that insertion of silicone-covered magnesium esophageal stent is a promising approach for treating BES.
基金
Supported by the National Natural Science Foundation of China,No.81371659,No.81571773,and No.81771943
Shanghai Municipal Health and Family Planning Commission,No.201640191