Lead halide perovskites exhibit unexceptionable photoelectric properties.However,these materials are unsatisfactory in terms of stability and toxicity.Herein,we report Rb7 Sb3 Cl16 as a new kind of lead free perovskite variants.This material can be easily obtained through hydrothermal reactions.The composition is determined through structure refinement,elemental analysis and X-ray photoelectron spectra.Rb7 Sb3 Cl16 exhibits a broad yellow emission at 560 nm,with a Stokes shift of 175 nm and a photoluminescence quantum yield(PLQY)around 26%.Rb7 Sb3 Cl16 also shows good thermal and water stability due to its inorganic composition.White light-emitting diodes(LEDs)are constructed by combining Rb7 Sb3 Cl16 as yellow phosphors,our previously reported Cs2 SnCl6:2.75%Bi as blue phosphors,and commercial UV LED chips as the excitation source,producing a white light with the Commission Internationale de’Eclairage(CIE)color coordinates at(0.39,0.38).
Lead halide perovskites exhibit unexceptionable photoelectric properties.However,these materials are unsatisfactory in terms of stability and toxicity.Herein,we report Rb7 Sb3 Cl16 as a new kind of lead free perovskite variants.This material can be easily obtained through hydrothermal reactions.The composition is determined through structure refinement,elemental analysis and X-ray photoelectron spectra.Rb7 Sb3 Cl16 exhibits a broad yellow emission at 560 nm,with a Stokes shift of 175 nm and a photoluminescence quantum yield（PLQY）around 26%.Rb7 Sb3 Cl16 also shows good thermal and water stability due to its inorganic composition.White light-emitting diodes（LEDs）are constructed by combining Rb7 Sb3 Cl16 as yellow phosphors,our previously reported Cs2 SnCl6:2.75%Bi as blue phosphors,and commercial UV LED chips as the excitation source,producing a white light with the Commission Internationale de’Eclairage（CIE）color coordinates at（0.39,0.38）.
基金
supported by the National Key R&D Program of China (2016YFB0700702)
the National Natural Science Foundation of China (51761145048, 61725401, and 51702107)
China Postdoctoral Science Foundation (2018M632843)
the Huazhong University of Science and Technology (HUST) Key Innovation Team for Interdisciplinary Promotion (2016JCTD111, 2017KFXKJC003)
Wuhan National High Magnetic Field Center