以自制的功能化氧化石墨烯(C-GO)/聚苯胺(PANI)复合材料为改性填料,对环氧树脂(EP)进行改性,制备了C-GO/PANI/EP复合涂料,研究了复合涂料的防腐性能和防腐机理。结果表明,当C-GO质量分数为3%时,复合涂料硬度最高,吸水率最低,防腐性能最佳。C-GO/PANI是通过填补EP表面的空隙,改善EP的屏蔽性能,阻止O2和H2O的渗入,从而提高EP的防腐性能。
The epoxy resin was modified using the self-made composites of functionalized graphene oxide/polyaniline as modification filler.The functionalized graphene oxide/polyaniline/epoxy resin composite coating were made.The anti-corrosion property and mechanism were studied.The results showed that,hardness and anti-corrosion property of the composite coating were the best and water absorption was the lowest when the content of the functionalized graphene oxide was 3%.The composites of functionalized graphene oxide/polyaniline could fill the surface interspace and improve the shielding property of epoxy resin,thus the anti-corrosion property of epoxy resin was improved.
作者
王博涛
宋军旺
郭睿
赵新法
WANG Bo-tao;SONG Jun-wang;GUO Rui;ZHAO Xin-fa(School of Chemical Engineering,Shaanxi Energy Institute,Xianyang 712000,Shaanxi,China;Key Laboratoryof Auxiliary Chemistry and Technology in Light Industry,Ministry of Education,Shaanxi University of Science and Technology,Xi'an 710021,Shaanxi,China)
出处
《合成材料老化与应用》
2019年第4期34-38,107,共6页
Synthetic Materials Aging and Application
基金
陕西重点研发计划资助(2017GY-185)
关键词
氧化石墨烯
功能化
聚苯胺
涂料
性能
graphene oxide
functionalized
polyaniline
coating
property