The low modulation bandwidth of deep-ultraviolet(UV) light sources is considered as the main reason limiting the data transmission rate of deep-UV communications. Here, we present high-bandwidth Ⅲ-nitride microlight-emitting diodes(μLEDs) emitting in the UV-C region and their applications in deep-UV communication systems. The fabricated UV-C μLEDs with 566 μm2 emission area produce an optical power of 196 μW at the 3400 A∕cm2 current density. The measured 3 dB modulation bandwidth of these μLEDs initially increases linearly with the driving current density and then saturates as 438 MHz at a current density of 71 A∕cm2, which is limited by the cutoff frequency of the commercial avalanche photodiode used for the measurement. A deep-UV communication system is further demonstrated. By using the UV-C μLED, up to 800 Mbps and 1.1 Gbps data transmission rates at bit error ratio of 3.8 × 10-3 are achieved assuming on-off keying and orthogonal frequency-division multiplexing modulation schemes, respectively.
The low modulation bandwidth of deep-ultraviolet（UV） light sources is considered as the main reason limiting the data transmission rate of deep-UV communications. Here, we present high-bandwidth Ⅲ-nitride microlight-emitting diodes（μLEDs） emitting in the UV-C region and their applications in deep-UV communication systems. The fabricated UV-C μLEDs with 566 μm2 emission area produce an optical power of 196 μW at the 3400 A∕cm2 current density. The measured 3 dB modulation bandwidth of these μLEDs initially increases linearly with the driving current density and then saturates as 438 MHz at a current density of 71 A∕cm2, which is limited by the cutoff frequency of the commercial avalanche photodiode used for the measurement. A deep-UV communication system is further demonstrated. By using the UV-C μLED, up to 800 Mbps and 1.1 Gbps data transmission rates at bit error ratio of 3.8 × 10-3 are achieved assuming on-off keying and orthogonal frequency-division multiplexing modulation schemes, respectively.
基金
Engineering and Physical Sciences Research Council(EPSRC)(EP/M01326X/1)