摘要
采用十六烷基三甲基溴化铵(CTAB)为模板的软模板法合成纳米聚吡咯(PPy)线,探究模板改变对合成纳米聚吡咯线的形貌及其热稳定性的影响。利用红外光谱仪(IR)、扫描电子显微镜(SEM)对其进行表征。结果表明:以CTAB为模板可以成功合成线形聚吡咯,扫描电镜显示纳米聚吡咯线微观形貌与加入的模板浓度有关,在模板浓度为8 CMC时合成的纳米聚吡咯线的微观形貌最好。
The nano-polypyrrole(PPy) wire was synthesized by soft template method using cetyltrimethylammonium bromide(CTAB) as template.The effects of template modification on the morphology and thermal stability of the synthesized nano-polypyrrole wire were investigated.It was characterized by infrared spectrometer(IR),scanning electron microscope(SEM).The results showed that linear polypyrrole could be successfully synthesized by using CTAB as template.Scanning electron microscopy showed that the morphology of nano-polypyrrole wire was related to the concentration of template added.The microstructure of nano-polypyrrole wire synthesized at the template concentration of 8 CMC was the best.
作者
安光密
吴会敏
李航
郑兴莉
尹晓刚
An Guangmi;Wu Huimin;Li Hang;Zheng Xingli;Yin Xiaogang(School of Chemistry and Materials Science,Guizhou Normal University,Guizhou Key Laboratory of Functional Materials Chemistry,Guiyang 550001,China)
出处
《山东化工》
CAS
2019年第15期3-4,7,共3页
Shandong Chemical Industry
基金
贵州省大学生创新创业训练计划项目(2018520169)