In this work, the generalizing of the finite element method (FEM) of thermoplastic prepreg insert injection molding composites was investigated. The specimens were prepared using glass fiber/polyamidc 6 (GF/PA6) inserted prepreg, and their characteristics were investigated and compared under ANSYS workbench program. The prediction of the bending initial fracture point under analytical tensile testing with interlayer on prepreg insert moldings was focused. It was found that the bending initial fracture point was applied to predict by matching the shear stress. There was obtained from analytical tensile testing and bending analysis. Therefore, it can be obtained the optimum of the clastic modulus ratio on the injection part/interlayer/insert part by using FEM via ANSYS workbench.
In this work, the generalizing of the finite element method(FEM) of thermoplastic prepreg insert injection molding composites was investigated. The specimens were prepared using glass fiber/polyamide 6(GF/PA6) inserted prepreg, and their characteristics were investigated and compared under ANSYS workbench program. The prediction of the bending initial fracture point under analytical tensile testing with interlayer on prepreg insert moldings was focused. It was found that the bending initial fracture point was applied to predict by matching the shear stress. There was obtained from analytical tensile testing and bending analysis. Therefore, it can be obtained the optimum of the elastic modulus ratio on the injection part/interlayer/insert part by using FEM via ANSYS workbench.
出处
《纤维复合材料》
CAS
2019年第2期10-14,共5页
Fiber Composites