The Zn-added ultrasonic assisted friction stir lap welding(UaFSLW) was carried out to improve the quality of dissimilar Al/Mg alloys joint. The effects of ultrasonic power on the joint quality were also investigated.The results indicated that the larger effective lap width and mixing region between Mg and Al(Mg/Al MR) were attained by Zn foil addition and external ultrasonic assistance. Compared with the conventional joint, the finer and better-distributed Mg-Zn IMCs placing the continuous Al-Mg IMCs were formed in the Mg/Al MR of the Zn-added UaFSLW joint. The Zn foil addition and external ultrasonic assistance significantly improved the tensile shear load of the joint, and the load was increased with the increase of the ultrasonic power. The maximum tensile shear load of 7.95 kN was attained, which was 52.6% larger than that of the conventional joint.
The Zn-added ultrasonic assisted friction stir lap welding(UaFSLW) was carried out to improve the quality of dissimilar Al/Mg alloys joint. The effects of ultrasonic power on the joint quality were also investigated.The results indicated that the larger effective lap width and mixing region between Mg and Al(Mg/Al MR) were attained by Zn foil addition and external ultrasonic assistance. Compared with the conventional joint, the finer and better-distributed Mg-Zn IMCs placing the continuous Al-Mg IMCs were formed in the Mg/Al MR of the Zn-added UaFSLW joint. The Zn foil addition and external ultrasonic assistance significantly improved the tensile shear load of the joint, and the load was increased with the increase of the ultrasonic power. The maximum tensile shear load of 7.95 kN was attained, which was 52.6% larger than that of the conventional joint.
基金
supported by the National Natural Science Foundation of China (No. 51874201)