In-situ composites based on dispersed poly (ethylene terephthalate) (PET) or polyamide (PA), and continuous polyethylene (PE) were prepared through a single screw extruder of Haake rheometer system with a rod-die relatively small in diameter. The extrudate was drawn at a drawing ratio of 3.1, and then quickly cooled in cold water. The specimens were obtained by injection molding at processing temperatures less than 190℃, far below the melting temperature of PET (265℃) and PA (230℃), which can maintain the solid state of PET and PA microfiber phase in the composites. Morphological observation with scanning electron microscopy (SEM) indicated that PET and PA can more or less form in-situ microfibers at compositions studied (0~20 wt pct PET or PA), and especially, PET and PA were almost deformed into fibers at the concentration of 15 wt pct. Tensile strength and modulus of the blends reinforced by PET or PA microfibers showed to be increased from the tensile test results. The most noticeable improvement of the tensile properties occurred at 15 wt pct of PET in PET/PE system, corresponding to the highest microfiber content, where the tensile strength reached 32.5 MPa, whereas only 19.5 MPa for the pure PE.
In-situ composites based on dispersed poly (ethylene terephthalate) (PET) or polyamide (PA), and continuous polyethylene (PE) were prepared through a single screw extruder of Haake rheometer system with a rod-die relatively small in diameter. The extrudate was drawn at a drawing ratio of 3.1, and then quickly cooled in cold water. The specimens were obtained by injection molding at processing temperatures less than 190℃, far below the melting temperature of PET (265℃) and PA (230℃), which can maintain the solid state of PET and PA microfiber phase in the composites. Morphological observation with scanning electron microscopy (SEM) indicated that PET and PA can more or less form in-situ microfibers at compositions studied (0~20 wt pct PET or PA), and especially, PET and PA were almost deformed into fibers at the concentration of 15 wt pct. Tensile strength and modulus of the blends reinforced by PET or PA microfibers showed to be increased from the tensile test results. The most noticeable improvement of the tensile properties occurred at 15 wt pct of PET in PET/PE system, corresponding to the highest microfiber content, where the tensile strength reached 32.5 MPa, whereas only 19.5 MPa for the pure PE.
基金
Thanks are kindly given to the Scientific and Technological Committee of Sichuan for financial support
We are also grate-ful for project subsidizing by the Special Funds for Major Basic Research (Contract No. G1999064805)
the National Natural Science