摘要
VO 2 thin films with good switching properties were prepared by controlling the annealing time and the annealing temperature in a vacuum system. The structural, optical and electrical properties of the samples were characterized by using XRD、XPS、UV-VIS and electrical measurements. The switching parameters of VO 2 thin film were investigated too. The results indicate that before and after phase transition the resistance of VO 2 thin films changes about three orders of magnitude, the variation of film transmittance of 40 % has been carried out with the absorptivity switching velocity of about 0.260 7 /min at 900 nm . The structural property of samples has been improved but the phase-transition properties have been decreased by increasing the annealing time and annealing temperature. The valence of V ions and the structure of samples have great effect on phase transition properties of VO 2 thin films. Discussion on the effects of annealing time and annealing temperature on the phase-transition temperature and hysteresis width shows that the best reasonable annealing time and annealing temperature can be achieved.
VO 2 thin films with good switching properties were prepared by controlling the annealing time and the annealing temperature in a vacuum system. The structural, optical and electrical properties of the samples were characterized by using XRD、XPS、UV-VIS and electrical measurements. The switching parameters of VO 2 thin film were investigated too. The results indicate that before and after phase transition the resistance of VO 2 thin films changes about three orders of magnitude, the variation of film transmittance of 40 % has been carried out with the absorptivity switching velocity of about 0.260 7 /min at 900 nm . The structural property of samples has been improved but the phase-transition properties have been decreased by increasing the annealing time and annealing temperature. The valence of V ions and the structure of samples have great effect on phase transition properties of VO 2 thin films. Discussion on the effects of annealing time and annealing temperature on the phase-transition temperature and hysteresis width shows that the best reasonable annealing time and annealing temperature can be achieved.
关键词
氧化钒薄膜
相变
薄膜结构
VO 2 thin film
Phase transition
Film structure
Valence state