The 60Co γ radiation effect on spherical open-porous polymethylphenylvinyl siloxane foam was studied in different atmospheres at room temperature. The physical and chemical behaviors of unirradiated and irradiated materials were studied by SEM, FTIR, TG (thermal gravity analysis), GC/MS(gas chromatography and mass spec -troscopy), etc. The present results indicate that the yields of gas products increase linearly with the dose increasing. Furthermore, some changes in material’s microscopic form, composition, structure and mechanical property were observed, but the maxi -mum thermal decomposition temperature of the sample alters little and the dose gives no effect on it.
The 60Co γ radiation effect on spherical open-porous polymethylphenylvinyl siloxane foam was studied in different atmospheres at room temperature. The physical and chemical behaviors of unirradiated and irradiated materials were studied by SEM, FTIR, TG (thermal gravity analysis), GC/MS(gas chromatography and mass spec -troscopy), etc. The present results indicate that the yields of gas products increase linearly with the dose increasing. Furthermore, some changes in material's microscopic form, composition, structure and mechanical property were observed, but the maxi -mum thermal decomposition temperature of the sample alters little and the dose gives no effect on it.
基金
Supported by the China Academy of Engineering Physics (CAEP Project No. 1999Z0503)
关键词
硅氧烷泡沫
Γ射线辐照
降解
Polymethylphenylvinyl siloxane foam, γ- ray irradiation, Radiation cross link-ing, Radiation degradation