摘要
采用差热分析 (DAT)研究了NiMnCo粉末触媒熔化和凝固过程中合金的变化规律 ;采用扫描电子显微镜、金相显微镜、X射线衍射分析仪揭示了粉末触媒的微观组织结构 ,并对粉末触媒合成金刚石的合成块断口及合成的金刚石进行了分析 ,从宏观。
The DAT behaviors of NiMnCo powder catalyst during melting and solidifying were studied. The micro structure of the catalyst was revealed through SEM, optical microscopy and X ray diffraction. The fracture of the synthetic diamond was analyzed. The property evaluation of NiMnCo catalyst was conducted from macro and micro anyles.