The synthesis and characterization of a series of novel poly(aryl amide imide)s based on o diphenyltrimellitic anhydride are described.The poly(aryl amide imide)s having inherent viscosities of 0.39-1.43dL/g in N methyl 2 pyrrolidinone at 30℃,were prepared by polymerization with aromatic diamines in N,N-dimethylacetamide and subsequent chemical imidization.All the polymers were amorphous,readily soluble in aprotic polar solvents such as DMAC,NMP,DMF,DMSO,and m cresol,and could be cast to form flexible and tough films.The glass trsanition temperatures were in the range of 284-336℃,and the temperatures for 5% weight loss in nitrogen were above 468℃.
The synthesis and characterization of a series of novel poly(aryl amide imide)s based on o diphenyltrimellitic anhydride are described.The poly(aryl amide imide)s having inherent viscosities of 0.39-1.43dL/g in N methyl 2 pyrrolidinone at 30℃,were prepared by polymerization with aromatic diamines in N,N-dimethylacetamide and subsequent chemical imidization.All the polymers were amorphous,readily soluble in aprotic polar solvents such as DMAC,NMP,DMF,DMSO,and m cresol,and could be cast to form flexible and tough films.The glass trsanition temperatures were in the range of 284-336℃,and the temperatures for 5% weight loss in nitrogen were above 468℃.
基金
FundedbytheNaturalScienceFoundatiionofHubeiProvince(2 0 0 0J0 2 4and 99A12 3)