摘要
The complex oxide Dy_(10)W_2O_(21) was synthesized by a solid-state reactionand isolated in cubic symmetry by an X-ray diffractometry (XRD) method. Differential scanningcalorimetry (DSC) measurements show that the compound is thermodynamically stable. The intrinsicthermal expansion coefficients were determined by extra-power powder X-ray diffractometry from roomtemperature to 1000 deg C: linear coefficient alpha-bar = 1.07 X 10^(-5) deg C^(-1) and bulkcoefficient beta-bar = 3.20 X 10^(-5) deg C^(-1). Dilatometry was used to measure the extrinsicthermal expansion coefficient (9.2 X 10^(-6) deg C^(-1)).
The complex oxide Dy_(10)W_2O_(21) was synthesized by a solid-state reactionand isolated in cubic symmetry by an X-ray diffractometry (XRD) method. Differential scanningcalorimetry (DSC) measurements show that the compound is thermodynamically stable. The intrinsicthermal expansion coefficients were determined by extra-power powder X-ray diffractometry from roomtemperature to 1000 deg C: linear coefficient alpha-bar = 1.07 X 10^(-5) deg C^(-1) and bulkcoefficient beta-bar = 3.20 X 10^(-5) deg C^(-1). Dilatometry was used to measure the extrinsicthermal expansion coefficient (9.2 X 10^(-6) deg C^(-1)).
基金
This work was financially supported by the National Natural Science Foundation of China (Nos. 29971004 and 20171006)
the Funds of Ministry of Education of China for Training Doctors (No. 20010008005)
the Assistant Plan to Key Young College's Teachers