The thermodynamic factor in diffusion in the L1_2-type non-stoichiometricintermetallic compounds Ni_3Ga and Pt_3In was derived from the experimentally measured activities ofGa and In, respectively. The results show that the thermodynamic factor in diffusion in the Ni_3Gaand Pt_3In compounds exhibits the maximum near the stoichiometric composition with the variation ofcomposition over the compound region. The values indicate strong interaction between Ni and Gaatoms, as well as Pt and In atoms, respectively, as expected in ordered alloys.
The thermodynamic factor in diffusion in the L1_2-type non-stoichiometricintermetallic compounds Ni_3Ga and Pt_3In was derived from the experimentally measured activities ofGa and In, respectively. The results show that the thermodynamic factor in diffusion in the Ni_3Gaand Pt_3In compounds exhibits the maximum near the stoichiometric composition with the variation ofcomposition over the compound region. The values indicate strong interaction between Ni and Gaatoms, as well as Pt and In atoms, respectively, as expected in ordered alloys.
基金
This project is jointly supported by the National Natural Science Foundation of China (No. 29871005)
the Science Foundation of Austria (No. P12962-CHE).