Autoigniting synthesis of gel from Ba(NO_3)_2, TiO(NO_3)_2 and C_6H_8O_7centre dot H_2O aqueous solution was investigated at an initial temperature of 600 deg C andtetragonal BaTiO_3 nanopowder with particle size of 80nm was prepared. It is indicated that thespecific surface area of the combustion product before and after calcinations is 14.74 m^2/g and12.49 m^2/g, respectively. The combustion wave is composed of solid phase reaction zone and gaseousphase flame reaction zone. The combustion flame temperature is 1 123 K derived from thermocouplemeasurement. The characteristics and densification behavior of the sol-gel autoigniting synthesizedBaTiO_3 nanopowder were investigated.
Autoigniting synthesis of gel from Ba(NO_3)_2, TiO(NO_3)_2 and C_6H_8O_7centre dot H_2O aqueous solution was investigated at an initial temperature of 600 deg C andtetragonal BaTiO_3 nanopowder with particle size of 80nm was prepared. It is indicated that thespecific surface area of the combustion product before and after calcinations is 14.74 m^2/g and12.49 m^2/g, respectively. The combustion wave is composed of solid phase reaction zone and gaseousphase flame reaction zone. The combustion flame temperature is 1 123 K derived from thermocouplemeasurement. The characteristics and densification behavior of the sol-gel autoigniting synthesizedBaTiO_3 nanopowder were investigated.