目前陶瓷废料堆积量较大,难以全部回收利用。采用抛光渣、压榨泥、废砖屑三种陶瓷废料为原料制备轻质保温泡沫陶瓷,研究三种陶瓷废料配比、发泡剂含量、烧成温度和保温时间对泡沫陶瓷试样性能的影响。最终采用60wt%的抛光渣、30wt%废砖屑和10wt%压榨泥为原料,添加0.6wt%的SiC作为发泡剂,在1160℃保温时间30 min的条件下制得体积密度0.41 g/cm^3、抗压强度3.5 MPa、导热系数0.14 W/(m·K)的泡沫陶瓷材料。研究采用100wt%陶瓷废料烧制泡沫陶瓷,为陶瓷废料综合利用提供了一条可行的途径。
At present,the amount of ceramic waste is too large to be fully recycled.Three kinds of ceramic wastes,such as polishing slags,press muds and waste brick scraps,were used as raw materials to fabricate lightweight thermal insulation foam ceramics.The influence of three kinds of ceramic waste ratio,foaming agent content,sintering temperature and holding time on the properties of foam ceramics were studied.Finally,the foam ceramic with bulk density of 0.41 g/cm^3,compressive strength of 3.5 MPa and thermal conductivity of 0.14 W/(m·K)was prepared by using 60wt%polishing slags,30wt%waste brick scraps and 10wt%press muds as raw materials and adding 0.6wt%SiC as foaming agent at 1160℃ for 30 min.100wt%ceramic wastes were used to fabricate foam ceramics.It provided a feasible way for the comprehensive utilization of ceramic wastes.
作者
赵威
王竹
戴永刚
南宁
ZHAO Wei;WANG Zhu;DAI Yong-gang;NAN Ning(Shaanxi Key Laboratory of Comprehensive Utilization of Tailings Resources,Shangluo University,Shangluo 726000,China;Guangdong KITO Ceramics Co.,Ltd.,Foshan 528031,China;School of Materials Science and Engineering,South China University of Technology,Guangzhou 510640,China)
出处
《硅酸盐通报》
CAS
北大核心
2019年第7期2288-2294,共7页
Bulletin of the Chinese Ceramic Society
基金
陕西省科技厅重点研发计划项目(2018GY-123)
商洛学院科研计划项目(15SKY022)
关键词
泡沫陶瓷
陶瓷废料
烧成工艺
发泡剂
foam ceramic
ceramic waste
sintering technique
foaming agent