摘要
The microstructure evolution and intergranular corrosion(IGC) behavior of high nitrogen martensitic stainless steels(MSSs) by partial replacing C by N were investigated by using microscopy, X-ray diffraction, nitric acid tests and double-loop electrochemical potentiokinetic reactivation(DL-EPR) tests. The results show that the partial replacement of C by N first reduces and then increases the size and content of precipitates in high nitrogen MSSs, and converts the dominant precipitates from M23C6 to M2N,furthermore first improves and then deteriorates the IGC resistance. The high nitrogen MSS containing medium C and N contents provides good combination of mechanical properties and IGC resistance.
The microstructure evolution and intergranular corrosion（IGC） behavior of high nitrogen martensitic stainless steels（MSSs） by partial replacing C by N were investigated by using microscopy, X-ray diffraction, nitric acid tests and double-loop electrochemical potentiokinetic reactivation（DL-EPR） tests. The results show that the partial replacement of C by N first reduces and then increases the size and content of precipitates in high nitrogen MSSs, and converts the dominant precipitates from M23C6 to M2N,furthermore first improves and then deteriorates the IGC resistance. The high nitrogen MSS containing medium C and N contents provides good combination of mechanical properties and IGC resistance.
基金
supported by the National Natural Science Foundation of China [grant numbers 51434004, U1435205, 51774074]
Fundamental Research Funds for the Central Universities [N172512033, N172507002]
Transformation Project of Major Scientific and Technological Achievements in Shenyang [grant number Z17-5-003]