基于3D-DIC对爆炸作用下碳纤维层合板的变形研究 被引量:6

Deformation of Carbon Fiber Laminates under Explosion Based on 3D-DIC
下载PDF
导出
摘要 针对3种不同铺层的碳纤维复合材料层合板,设计了开放式爆炸加载实验,研究不同的炸药质量和爆炸距离下层合板的动态力学行为。基于两台高速相机,搭建了高速三维变形场的实验测量系统,记录层合板在爆炸作用下动态变形过程。通过三维数字图像相关方法(3D-DIC)软件计算得到层合板在冲击波作用下的动态位移场和应变场。研究发现:层合板在弱冲击波作用下只发生弹性变形,正交铺层和准均质铺层均表现出良好的抗冲击能力;在强冲击波作用下层合板会产生分层、基体开裂、纤维断裂等形式的损伤,铺层顺序对损伤形式有很大影响。 An open explosion loading experiment was designed for three differently laminated carbon fiber composite laminates to study the dynamic mechanical behavior of the laminates under different explosive masses and explosive distances.Based on two high-speed cameras,an experimental measurement system for high-speed three-dimensional deformation field was built,and the images of the dynamic deformation process of the laminates under the action of the explosion were recorded.The dynamic displacement field and strain field of the laminates under the shock wave were calculated by 3D-DIC software.The results show that the laminates only undergo elastic deformation under low shock wave,and the orthogonal layer and the quasi-homogeneous layer have good impact resistance;under the action of high shock wave,the laminates will cause damage in the form of delamination,matrix cracking,fiber breakage,etc.The order of the layup has a great influence on the form of damage.
作者 刘青青 郭保桥 石晨 陈鹏万 LIU Qingqing;GUO Baoqiao;SHI Chen;CHEN Pengwan(State Key Laboratory of Explosion Science and Technology,Beijing Institute of Technology,Beijing 100081,China)
出处 《高压物理学报》 EI CAS CSCD 北大核心 2019年第6期138-145,共8页 Chinese Journal of High Pressure Physics
基金 国家自然科学基金(11472047)
关键词 碳纤维层合板 三维数字图像相关方法 爆炸 损伤 破坏 carbon fiber reinforced laminate 3D-DIC blasting loading damage failure
  • 相关文献

参考文献3

二级参考文献25

共引文献151

同被引文献51

引证文献6

二级引证文献16

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部