摘要
The properties of resin transfer molding(RTM)cyanate ester and its T800 grade carbon fiber composites were studied with the rheometer,differential scanning calorimetry(DSC),FT-IR,dynamic mechanical analyzer(DMA),thermal gravimetric analysis(TGA),mechanical property testing,and scanning electron microscopy(SEM).The results showed that the temperature of cyanate ester suitable for RTM process was 70℃.Curing process of the resin was 130℃/2 h+160℃/2 h+200℃/2 h+220℃/4 h.Glass transition temperature and heat decomposition temperature of the cured resin are 289℃and 415℃,respectively.Mechanical properties of T800/RTM cyanate composites are 13.5%higher than that of T700/RTM cyanate composites and equal to that of T800/Prepreg cyanate composites.Tg of T800/RTM cyanate composites was proved to be 291℃.Fracture pattern of the composites was flat,which proved excellent interface properties between fiber and resin in this composite.